Olan Glass Beads Dictionary


Index of Olan Glass Beads Dictionary

Soda-Lime Glass

A

Al2O3(Composition %):   (max.3.2%)               0.4

C

B2O3                                                               0.0

C

Crush Strength(psi):    >30,000

CaO   8.0-10.0%              9.8

 

CAS # 65997-17-3 (Glass Beads)

CAS # 7631-86-9((SiO2

CAS # 1313-59-3 (Na2O

CAS # 1305-78-8 (CaO)

CAS # 1309-48-4 (MgO)

CAS # 1344-28-1 (Al2O3)

Components(Main, weight in %):

       SiO2     71.0-73.0%

       Na2O    13.0-14.5%

       CaO      8.0-10.0%

       MgO     Max.4.2%

       Fe2O3           0.2%

       Al2O3          Max.3.2%

Coefficient of Friction:                                     0.9-1.0

 

D

Dielectric Constant, 22ºC,106Hz                    6.9

Diameter(Microns) and Mesh(#)

       38um=400# 

       45um=325# 

       53um=270# 

       63um=230# 

       75um=200# 

       90um=170# 

       106um=140# 

       125um=120# 

       150um=100# 

       180um=80# 

       212um=70# 

       250um=60# 

       300um=50# 

       425um=40# 

       355um=45# 

       500um=35# 

       600um=30# 

       710um=26# 

       850um=20# 

       1000um=18# 

       1180um=16# 

       1400um=14# 

       1700um=12# 

       2000um=10# 

       2360um=8# 

       2800um=7# 

       3350um=6# 

       4000um=5# 

 

E

EINECS # 266-046-0

Expansion Coefficient, in/in/ºCX10-7                     90

 

F

Fe2O3 /FeO                                                        0.2%

 

 

H

Hardness (Moh):   5-6                                          6.0

 

 

I

(Free) Iron Content:  max. 0.1%

K

K2O                                                                    0.1%

L

Loss Tangent,  22ºC,106Hz                               0.0085

Leachate PH                                                           9.4

Leach Conductivity,(mmho/cm)                               101.0

Leach Concentrations,(mg/cc)

 

M

MgO   Max.4.2%:             3.3

 

 

N

Na2O(Composition %) :    13-14.5                         13.7

O

Oil Absorption*(g oil/100g. spheres)ASTM D-1483 :    18

P

PH:   9-10

R

Refractive Index:   1.51-1.64,                                      1.51

Rigidity  Modulus, 106PSI                                        4.3

 

S

Specific Gravity(g/cm3):    2.4-2.6,                          2.5

Softening Point, °C:       700-800                            704

SiO2(Composition %)    :   71-73                            72.5

T

Thermal Conductivity(cal/(sec)(cm2)(ºC/cm)at 500ºC               0.0036

Total Alkali                                                                25.7

                 Calcium                                                   18.1

                 Boron                                                       Trace

                 Silica                                                        5.4

V

Vol. Resistivity, 25ºC, ohm-cm                            6.5x1012

 

 

Y

Young's Modulus, 106PSI                                   10.0